Residual Stress and Its Effects on Fatigue and Fracture
Proceedings of a Special Symposium held within the 16th European Conference of Fracture - ECF16, Alexandroupolis, Greece, 3-7 July, 2006
Price for Eshop: 2520 Kč (€ 100.8)
VAT 0% included
New
E-book delivered electronically online
E-Book information
Annotation
Simplified fracture mechanics based assessment methods are widely used by the industry to determine the structural integrity significance of postulated cracks, manufacturing flaws, service-induced cracking or suspected degradation of engineering components under normal and abnormal service loads. In many cases, welded joints are the regions most likely to contain original fabrication defects or cracks initiating and growing during service operation. Various procedures provide upper bound residual stress profiles for various classes of welded joints that can be used in fracture assessments, but these often give very conservative results. Recently, the option to use more realistic profiles has been adopted, but only where such profiles are based on finite element residual stress simulations supported by detailed residual stress measurements. Rapid advances in the capability of residual stress measurement techniques, such as the contour and deep hole drilling techniques as well as the neutron and synchrotron X-ray diffraction methods, now readily allow residual stresses and strains to be mapped on defined planes within a structure. The contents of this book have been grouped into three topic areas covering theoretical /numerical and experimental analyses of residual stress and its effects on fatigue and fracture.
Ask question
You can ask us about this book and we'll send an answer to your e-mail.